FiberSatin Filament - 1.75 mm - 0.85 kg
FiberSatin Filament - 1.75 mm - 0.85 kg
Fiberlogy FiberSatin is an innovative 3D printing filament that enables the creation of elegant, semi-matte prints with a finish resembling professional materials. With its strong layer adhesion and slightly glossy surface, the filament effectively masks common additive manufacturing imperfections, such as visible layer lines.
FiberSatin stands out with its unique, pleasant-to-touch texture, similar to carbon fiber filaments. It diffuses light, giving prints a subtle shine and semi-matte effect that make models look both aesthetic and professional. The material is easy to print, fully compatible with Fiberlogy EASY PLA profiles, ensuring consistent and repeatable results even for more complex projects.
FiberSatin is perfect for decorative interior prints such as vases, phone stands, jewelry, or Christmas ornaments. Its elegant, semi-matte finish adds a distinctive character to any project. However, it should be noted that the material has relatively low thermal resistance and no UV resistance, making it best suited for indoor use.
Fiberlogy FiberSatin is the ideal filament for users seeking an easy-to-print PLA with a unique semi-matte finish and elegant visual effect – perfect for artistic and decorative 3D projects.
Premium Raw Materials
NatureWorks is a US-based company and one of the largest and most renowned producers of biopolymers worldwide, and above all – polylactic acid (PLA). Their flagship product, Ingeo
Print settings
- Printing temperature200-230°C
- Bed temperature60°C
- Build surfaceSmooth PEI, Textured PEI, Glass
- Drying conditions40°C / 4h
- Enclosurenot required
- Cooling fan75-100%
Tips and recommendations
- Possible bed damage:Due to strong adhesion to the surface, printing directly on the bed or glass is not recommended, as this may cause damage. We recommend using adhesives or masking tape.
- Filament swelling:During loading and printing, the extruded material may show swelling. This is a completely natural effect caused by the surface tension of the polymers in the filament.
Properties
- Density1.2 g/cm³
- Tensile Strength @ Yield48 MPa (ASTM D882)
- Tensile Strength @ Break50 MPa (ASTM D882)
- Tensile Modulus2500 MPa (ASTM D882)
- Elongation @ Yield4% (ASTM D882)
- Izod Impact Strength (Notched) @ 23℃4 kJ/m2 (ISO180)
- Heat Distortion Temperature @ 0.45 MPa55°C (ASTM D648)
- Glass Transition Temperature55 - 60°C (DSC)